dc.description.abstractA new thermoelectric material for the generation of electricity above room temperature has been prepared. It is constructed of innershield cored wire, a crystalline material such as Cs2CoCl4 and constantan. Its average Seebeck coefficient was measmed to be α ~830μV/K, resistivity has been moderate at around ρ~ 3x10-2Ωcm, thermal conductivity κ~1.03x10-2W/mK, yield η~0.2255 and figure of merit Z~5.16x10-3K-1 for a temperature difference ∆T~422K, where the high temperature was Th~736K and the cold temperature Tc~314K. These results were compared with those obtained from materials commercially prepared for these same aims. According to the spectroscopic X-rays analysis, the material is made up of Cs3CoCl5, Fe1.874Sn0.096O3, Co6C(CO)12S2, and Ba4In6O13 whose respective crystalline structures are tetragonal, hexagonal, monoclinic and orthorhombic.en_US
dc.description.abstractSe ha encontrado un nuevo material termoeléctrico para la generación de electricidad a temperaturas sobre la del ambiente. El mismo se construye a partir de alambres con alma fundente, material cristalino tal como Cs2CoCl4 y constantán. Se ha medido su coeficiente de Seebeck promedio α ~830μV/K , resistividad ρ~ 3x10-2Ωcm, conductividad térmica κ~1.03x10-2W/mK, rendimiento η~0.2255 y figura de mérito Z~5.16x10-3K-1 a una diferencia de temperatura ∆T~422K, donde la temperatura de la parte caliente Th~736K y en la parte fría Tc~314K. Estos resultados fueron comparados con los que se obtienen de materiales comerciales preparados para estos mismos fines. Según el análisis espectroscópico de rayos X, el material se compone de Cs3CoCl5, Fe1.874Sn0.096O3, Co6C(CO)12S2 y Ba4In6O13 cuyas respectivas estructuras cristalinas fueron tetragonal, hexagonal, monoclínica y ortorrómbica.en_US
dc.language.isoEspañolen_US
dc.titleGeneración y aprovechamiento de energía termoeléctricaen_US
dc.typeThesisen_US
dc.rights.licenseAll rights reserveden_US
dc.rights.holder(c) 2004 Carlos Eduardo Cuéllar-Santanillaen_US
dc.contributor.committeeMoisés, Orengo
dc.contributor.committeeMéndez, Rubén
dc.contributor.representativeWalker-Ramos,Uroyoán R.
thesis.degree.levelM.S.en_US
thesis.degree.disciplinePhysicsen_US
dc.contributor.collegeCollege of Arts and Science - Scienceen_US
dc.contributor.departmentDepartment of Physicsen_US
dc.description.graduationYear2004en_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

  • Theses & Dissertations
    Items included under this collection are theses, dissertations, and project reports submitted as a requirement for completing a degree at UPR-Mayagüez.

Show simple item record

All rights reserved
Except where otherwise noted, this item's license is described as All Rights Reserved