Show simple item record

dc.contributor.advisorPerales-Pérez, Oscar J.
dc.contributor.authorCabán-Nevárez, Rebeca B.
dc.date.accessioned2019-08-12T15:57:41Z
dc.date.available2019-08-12T15:57:41Z
dc.date.issued2019-07-08
dc.identifier.urihttps://hdl.handle.net/20.500.11801/2507
dc.description.abstractIn the present study, the effect of ultrasonication treatment time on talc particles’ morphology, crystallite size, dimensions, structure and specific surface area was investigated. Additionally, the effect of talc as a filler material in chitosan/talc nanocomposite films’ barrier, mechanical and moisture absorption properties was studied, as a function of talc crystal size and concentration. It was found that treating talc particles through ultrasonication is effective to reduce their average crystallite size, as well as decrease both the lateral dimension and the thickness of the talc platelets (delamination), while maintaining its structural coherence and crystallinity. The ultrasonication treatment was also successful in increasing the specific surface area and it was determined that the flaky, platelet like morphology of talc was preserved throughout all treatment times. Upon addition of talc to the chitosan film, up to 16% and 24% increase in Modulus of elasticity (stiffness) was found, for the larger and smaller talc crystal size, respectively. A small increase in the Ultimate Tensile Strength of the films was observed for the 5% loading in both set of films, with values of 92-94 MPa. The water vapor permeability of the films was determined to slightly decrease (4-5%) with the addition of smaller crystal size talc, at 3 and 5% loadings. The water sensitivity of the films was improved, independent of talc crystal size and for all concentrations, as it was observed that the moisture absorption percent notably decreased (18-24% maximum reduction). Chitosan-talc nanocomposites show some promise as an emerging food packaging bioplastic due to its strength, stiffness and decreased water sensitivity. However, additional work is needed on the film synthesis method to improve its barrier properties and potentially compete with traditional food packaging plastics.en_US
dc.language.isoenen_US
dc.subjectNanocompositeen_US
dc.subjectTalcen_US
dc.subjectChitosanen_US
dc.subjectFood packagingen_US
dc.subjectBioplasticen_US
dc.subjectNanotechnologyen_US
dc.subjectBiopolymeren_US
dc.subjectFood scienceen_US
dc.subjectMaterial scienceen_US
dc.subject.lcshChitosanen_US
dc.subject.lcshTalcen_US
dc.subject.lcshNanocomposites (Materials)en_US
dc.subject.lcshUltasonicsen_US
dc.subject.lcshFood -- Packagingen_US
dc.titlePreparation and characterization of Chitosan/talc nanocomposite films for food packaging applicationsen_US
dc.typeThesisen_US
dc.rights.holder(c) 2019 Rebeca B. Cabán-Nevárezen_US
dc.contributor.committeePérez Muñoz, Fernando
dc.contributor.committeeRomán Velázquez, Felix R.
dc.contributor.representativeToledo Feria, Freya M.
thesis.degree.levelM.S.en_US
thesis.degree.disciplineFood Science and Technology Programen_US
dc.contributor.collegeCollege of Agricultural Sciencesen_US
dc.contributor.departmentDepartment of Food Science and Technologyen_US
dc.description.graduationSemesterSummeren_US
dc.description.graduationYear2019en_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

  • Theses & Dissertations
    Items included under this collection are theses, dissertations, and project reports submitted as a requirement for completing a degree at UPR-Mayagüez.

Show simple item record

(c) 2019 Rebeca B. Cabán-Nevárez
Except where otherwise noted, this item's license is described as All Rights Reserved