dc.description.abstractIn this study, poly (styrene-isobutylene-styrene) (SIBS) was characterized using thermogravimetric analysis. The thermal behavior of three types of SIBS, with different average number molecular weight, Mn , and polystyrene weight percent, are discussed as a function of sulfonation level and substitution with different ions (Ba+2, Ca+2, and Mg+2). For unsulfonated samples, a decrease in the degradation temperature was observed with an increase in Mn, for 30 % polystyrene by weight. Also, a decrease in the degradation temperature was observed with an increase in percent polystyrene with Mn of 100,000 g/mol. At high sulfonation levels, the backbone degradation temperature of the studied polymers increased up to a constant value, suggesting morphological similarities. The weight loss stage corresponding to the degradation of sulfonic groups was not observed in sulfonated polymers cross-linked with cations; however, two new weight loss stages are observed, which are attributed to the loss of cations and sulfonic groups. They are lost in two stages due to different coordination of the cations. SIBS with 15 % polystyrene by weight and Mn of 100,000 g/mol has a higher polymer backbone degradation temperature when compared to the other two studied SIBS, thus it can be considered more thermally stable.
dc.language.isoenen_US
dc.subjectThermogravimetric characterizationen_US
dc.subjectPoly (styrene-isobutylene-styrene)en_US
dc.subjectTriblock copolymersen_US
dc.subject.lcshThermogravimetryen_US
dc.subject.lcshTriblock copolymersen_US
dc.subject.lcshSulfonationen_US
dc.subject.lcshPolystyreneen_US
dc.titleThermogravimetric characterization of polystyrene-based, triblock copolymers: effects of sulfonation, counter-ion substitution, number average molecular weight, and polystyrene weight fractionen_US
dc.typeProject Reporten_US
dc.rights.licenseAll rights reserveden_US
dc.rights.holder(c) 2010 Gretselle F. Carreras Alvaradoen_US
dc.contributor.committeeColón, Guillermo
dc.contributor.committeeEstévez, L. Antonio
dc.contributor.representativeRivera, Luis A.
thesis.degree.levelM.E.en_US
thesis.degree.disciplineChemical Engineeringen_US
dc.contributor.collegeCollege of Engineeringen_US
dc.contributor.departmentDepartment of Chemical Engineeringen_US
dc.description.graduationYear2010en_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

  • Theses & Dissertations
    Items included under this collection are theses, dissertations, and project reports submitted as a requirement for completing a degree at UPR-Mayagüez.

Show simple item record

All rights reserved
Except where otherwise noted, this item's license is described as All Rights Reserved