dc.description.abstractOur objective is to study the growth mechanism of Ni nanostructures supported in microporous materials using X-ray diffraction. Since only the surface atoms of a catalyst are active, our aim is to find the optimum synthesis conditions for the formation of small Ni nanostructures. A state-of-the art XRD attachment called Reactor X was used to study the growth of the Ni nanostructures in situ. Our main focus was the study of the calcination and reduction of nickel acetate, as Ni metal precursor, impregnated into the one-dimensional channels of microporous VPI-8 and mordenite. Using the Reactor X we observed in the XRD diffraction patterns the appearance of nickel oxide (NiO) and Ni peaks during the calcination and reduction reactions, respectively. Among the most significant findings we found that the optimal reduction temperature that leads to the formation of metallic Ni crystals depends significantly on the metal loading and on the calcination.
dc.description.abstractNuestro objetivo es estudiar el crecimiento de nanoestructuras de Ni ancladas en materiales microporosos mediante difracción de rayos X. Debido que sólo aquellas partículas que se encuentran en la superficie de un catalizador son catalíticamente activas, queremos encontrar las condiciones óptimas que llevan a la formación de nanoestructuras de Ni pequeñas. El aditamento de XRD llamado Reactor X fue utilizado para estudiar el crecimiento de las nanoestructuras de Ni in situ. Nuestro objetivo principal era el estudio de la calcinación y reducción de acetato de níquel impregnado en canales unidimensionales de materiales microporos como VPI-8 y mordenita. De los difractogramas de XRD, observamos la aparición de los picos de óxido de níquel (NiO) y Ni durante la calcinación y reducción, respectivamente. Encontramos que la temperatura de reducción, que lleva a la formación de cristales metálicos de Ni depende significativamente de la cantidad de Ni que ha sido impregnada y de la calcinación.
dc.language.isoenen_US
dc.subjectNi nanostructuresen_US
dc.subjectNickel acetateen_US
dc.subject.lcshNickel--Synthesisen_US
dc.subject.lcshX-rays--Diffractionen_US
dc.subject.lcshZeolite catalystsen_US
dc.subject.lcshMordeniteen_US
dc.titleIn situ diffraction studies of Ni nanostructure growth using microporous materials as supportsen_US
dc.typeDissertationen_US
dc.rights.licenseAll rights reserveden_US
dc.rights.holder(c) 2009 Angel G. Santos-Riveraen_US
dc.contributor.committeeCardona-Martínez, Nelson
dc.contributor.committeeHernandez-Maldonado, Arturo
dc.contributor.committeeRinaldi, Carlos
dc.contributor.representativePares-Matos, Elsie I.
thesis.degree.levelPh.D.en_US
thesis.degree.disciplineChemical Engineeringen_US
dc.contributor.collegeCollege of Engineeringen_US
dc.contributor.departmentDepartment of Chemical Engineeringen_US
dc.description.graduationYear2009en_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

  • Theses & Dissertations
    Items included under this collection are theses, dissertations, and project reports submitted as a requirement for completing a degree at UPR-Mayagüez.

Show simple item record

All rights reserved
Except where otherwise noted, this item's license is described as All Rights Reserved